查看文章

The suspension plasma spray (SPS) process was used to produce coatings from yttria-stabilized zirconia (YSZ) powders with median diameters of 15 μm and 80 nm. The powder-ethanol suspensions made with 15-μm diameter YSZ particles formed coatings with microstructures typical of the air plasma spray (APS) process, while suspensions made with 80-nm diameter YSZ powder yielded a coarse columnar microstructure not observed in APS coatings. To explain the formation mechanisms of these different microstructures, a hypothesis is presented which relates the dependence of YSZ droplet flight paths on droplet diameter to variations in deposition behavior. The thermal conductivity (k _th) of columnar SPS coatings was measured as a function of temperature in the as-sprayed condition and after a 50 h, 1200 °C heat treatment. Coatings produced from suspensions containing 80 nm YSZ …