Modified 9Cr-1Mo ferritic steel (T91/P91) has been subjected to a series of heat treatments consisting of soaking for 5 minutes at the selected temperatures, starting from the α-phase region (1073 K) to the γ + δ-phase region (1623 K), followed by oil quenching. Hardness measurements, microstructural features, and grain-size measurements by the linear-intercept method have been used for correlating them with the ultrasonic parameters. Ultrasonic velocity and attenuation measurements, and spectral analysis of the first backwall echo have been used for characterization of the microstructures obtained by various heat treatments. As the soaking temperature increased above Ac ₁, the ultrasonic velocity decreased because of the increase in the volume fraction of martensite in the structure. There were sharp changes in the ultrasonic velocities corresponding to the two critical temperatures, Ac …