查看文章

The large‐scale application of sodium/potassium‐ion batteries is severely limited by the low and slow charge storage dynamics of electrode materials. The crystalline carbons exhibit poor insertion capability of large Na⁺/K⁺ ions, which limits the storage capability of Na/K batteries. Herein, porous S and N co‐doped thin carbon (S/N@C) with shell‐like (shell size ≈20–30 nm, shell wall ≈8–10 nm) morphology for enhanced Na⁺/K⁺ storage is presented. Thanks to the hollow structure and thin shell‐wall, S/N@C exhibits an excellent Na⁺/K⁺ storage capability with fast mass transport at higher current densities, leading to limited compromise over charge storage at high charge/discharge rates. The S/N@C delivers a high reversible capacity of 448 mAh g^‐1 for Na battery, at the current density of 100 mA g^‐1 and maintains a discharge capacity up to 337 mAh g^‐1 at 1000 mA g^‐1. Owing to shortened diffusion pathways …