In this study, two similar, commercial polycrystalline Ni-based disk superalloys (LSHR and ME3) were creep tested at 760 °C and 552 MPa to approximately 0.3% plastic strain. LSHR consistently displayed superior creep properties at this stress/temperature regime even though the microstructural characteristics between the two alloys were comparable. High resolution structural and chemical analysis, however, revealed significant differences between the two alloys among active γ′ shearing modes involving superlattice intrinsic and extrinsic stacking faults. In ME3, Co and Cr segregation and Ni and Al depletion were observed along the intrinsic faults - revealing a γ′ to γ phase transformation. Conversely in LSHR, an alloy with a higher W content, Co and W segregation was observed along the intrinsic faults. This observation combined with scanning transmission electron microscopy (STEM) simulations …