Carbon/carbon (C/C) composite and Ti6Al4V alloy (wt%) were successfully brazed with graphene nanosheets strengthened AgCuTi filler (AgCuTiG). Graphene nanosheets (GNSs) with low CTE and high strength were dispersed into AgCuTi filler by ball milling. The interfacial microstructure was systematically characterized by varieties of analytical means including transmission electron microscopy (TEM). Results show that typical interfacial microstructure of the joint brazed at 880 °C for 10 min is a layer structure consisting of (Ti6Al4V/diffusion layer/Ti2Cu + TiCu + Ti3Cu4 + TiCu4/GNSs + TiCu + TiC + Ag(s,s) + Cu(s,s)/TiC/C/C composite). The interfacial microstructure and mechanical properties of brazed joints changed significantly as temperature increased. High temperature promoted the growth of TiCu and TiC phases, which were attached to GNSs. Meanwhile, the diffusion layer and primary reaction layers …