The wear behaviour of thin steel wires has been analyzed under oscillating sliding conditions in crossed cylinders contact geometry. The focus of this analysis was the influence of the crossing angle between the wires on the wear. The wires used had 0.45mm in diameter and the material was cold-drawn eutectoid carbon steel (0.8% C) with a tensile strength higher than 2800MPa. Two different types of tests were carried out, the first one representing the influence of the crossing angle for a constant load and the second one representing the influence of the crossing angle with constant contact pressure. In the first type of tests it was seen that as the contact angle decreases the contact pressure decreases too and hence less energy specific wear resistance is observed. As a consequence less wear is produced, thus increasing the life of the wires. In the second type of tests it was seen that with constant contact …