The corrosion behaviour of Mg-0.3Ce, Mg-0.41Dy, Mg-0.63Gd, Mg-1.44Nd and Mg-1.43La (wt.%) alloys in 3.5 wt% NaCl solution was investigated using electrochemical tests. The as-cast microstructures of the Mg-RE alloys were characterized by the presence of second phases (Mg_xCe, Mg₄₁Dy₅, Mg₁₂Gd, Mg₁₂Nd, Mg₄₁Nd₅, Mg₂₄Nd and Mg₁₂La) with different volume fraction and distribution. Results show that the corrosion mechanism was altered from uniform to localized corrosion mechanism depending on the specific RE alloying elements. The corrosion resistance of the Mg-RE alloys is increasing in the following order: Mg-1.43La, Mg-1.44Nd, Mg-0.3Ce, Mg-0.63Gd and Mg-0.41Dy. Accordingly, the corrosion morphology in the best resistant Mg-0.41Dy alloy and the worst Mg-1.43La alloy were observed and compared after 2h and 24 h of immersion using SEM-EDS, XPS and XRD analysis. The formation …