查看文章

Two different approaches were tried for an improvement of the cycle performance of Li–S cells: (1) A mixed polymer binder system of polyvinyl pyrrolidone (PVP) and polyethyleneimine (PEI) was developed to maintain the initial morphology of the carbon electrodes, the positive electrode of the Li–S cells, during charge–discharge cycles; (2) a tetrabutylammonium (TBA)-based mixed salt system was applied to an organic liquid electrolyte of the Li–S cells to change certain chemical reactions of polysulfides in the electrolyte solutions. The Li–S cells with PEI showed a significant improvement in cycle performance as well as in discharge capacity, compared with the Li–S cells using PVP only. The discharge capacity at the 50th cycle was found to be ∼580mAh/g-sulfur, 83% of an initial capacity (∼720mAh/g-sulfur), at a high current density of 2.0mAcm⁻². It was observed that the Li–S cells with a mixed electrolyte of 0 …