Introducing {10-12} tension twin lamellas has proved to be the most effective strategy to enhance the performance of Mg alloys. Twins can provide the preferential nucleation sites for recrystallization, hence twinning induced grain refinement can result in higher strength material based on Hall-Petch Effect. In addition, twinning can also modify the crystallographic c-axis distribution in wrought Mg alloys resulting in lower plastic anisotropy. Accordingly, in the present work, the twinning evolution in the Mg-0.5 Ca (wt.%) alloy at room and cryogenic temperature was critically investigated. The samples were subjected to pre-compression (5%) at room temperature and-150 C at the strain rate of 10-3 s-1. The microstructural and textural characterization was carried out using OM, SEM and EBSD to emphasize the twinning evolution during compression at room and low temperatures. The local lattice distortion and the …