Excellent damping capacities were observed in pure Mg and hypoeutectic Mg–Ni alloys. Two damping peaks (P₁,P₂) were found at 100°C and 230°C, respectively. P₁ was a newly detected damping peak, which was considered to derive from the movement of dislocations; it has great significance for practical applications.