Hot corrosion studies of thermal barrier coatings (TBCs) with different YSZ/LaMgAl₁₁O₁₉ (LaMA) composite coating top coats were conducted in 50 wt.% Na₂SO₄ + 50 wt.% V₂O₅ molten salt at 950 °C for 60 h. Results indicate that TBCs with composite coating top coats exhibit superior oxidation and hot corrosion resistances to the TBC with the traditional YSZ top coat, especially for which has a LaMA overlay. The presence of LaMA can effectively restrain the destabilization of YSZ at the expense of its own partial degradation. The hot corrosion mechanism of LaMA coating and the composite coatings have been explored.