The room-temperature plastic deformation behavior of pure Zn and Zn-Ag (0–2.2 at.%) biodegradable alloys has been investigated via uniaxial in situ micro-pillar compression tests performed within a scanning electron microscope. The critical resolved shear stresses (CRSS) were quantified as a function of micro-pillar diameter. The compression of single crystal micro-pillars was performed at various strain rates in carefully selected grains, the crystallographic orientation of which facilitates deformation either via basal 0001< 11 2¯ 0> or prismatic 10 1¯ 0< 11 2¯ 0> slip. The CRSS values increased with decreased micro-pillar diameter, revealing a more pronounced size effect in pure Zn deformed via basal slip. The observed solid solution strengthening effect in Zn-Ag alloys with increasing Ag content was associated with a CRSS increase from 26.6 MPa to 37.0 MPa (by∼ 40%) in the basal slip system and from 99.1 …