查看文章

Thermally stable high-entropy alloys (HEAs) consisting of a high density of coherent precipitates show a great potential for high-temperature applications. In this work, we systematically investigated the phase stability and coarsening kinetics of L1₂-type coherent precipitates in a Ni-30Co-13Fe-15Cr-6Al-6Ti-0.1B (at.%) HEA isothermally aged at 800, 900 and 1000 °C. Aged microstructures in the grain interiors under this temperature range were essentially dominated by the uniform precipitation of multicomponent L1₂ (Ni, Co, Fe, Cr)₃(Ti, Al)-type precipitates. The coarsening kinetics of these intragranular L1₂ precipitates were quantitatively determined, which were adequately characterized by the classical Lifshitz-Slyozov-Wagner model. The activation energy for coarsening was determined to be 378 kJ/mol, which is relatively higher than that of conventional Ni or Co-based superalloys, suggesting a slow elemental …