The influence of applied stress on the measurement of hardness and elastic modulus using nanoindentation methods has been experimentally investigated using special specimens of aluminum alloy 8009 to which controlled stresses could be applied by bending. When analyzed according to standard methods, the nanoindentation data reveal changes in hardness with stress similar to those observed in conventional hardness tests. However, the same analysis shows that the elastic modulus changes with stress by as much as 10%, thus suggesting that the analysis procedure is somehow deficient. Comparison of the real indentation contact areas measured optically to those determined from the nanoindentation data shows that the apparent stress dependence of the modulus results from an underestimation of the contact area by the nanoindentation analysis procedures.