In this work, the influence of different Ti additions on microstructure and property in Cu-Cr alloys has been studied and the primary relationship of processing-microstructure-property in Cu-Cr-Ti alloy has been constructed via the CALPHAD-based Integrated Computational Materials Engineering (ICME) approach and experimental validation. The peak-aged Cu-0.5Cr-0.2Ti alloy offers an excellent combination of hardness 192.6 HV, tensile strength 629.3 MPa, yield strength 603.0 MPa, electrical conductivity 51.3 %IACS and elongation 10.9 %. The calculated results suggest that the addition of Ti could promote the nucleation and hinder the growth of Cr precipitate in Cu-Cr-Ti alloys during aging treatment, which may promote the homogeneous formation of small-size precipitate Cr and improve the strength of the Cu-Cr alloy. Microstructural characterization has validated the calculation results and revealed that the …