investigated in this study. The experimental results revealed that SLM 316L SS could be
sensitized at 650° C as the treatment duration was larger than 6 h. Formation of the
precipitated phases that accelerated by the sub-grain boundaries was responsible for the
high susceptibility of SLM 316L SS to intergranular corrosion.