… the measurement of indentation crack lengths in air. … ceramic and glass fracture properties
using indentations this work will present and evaluate an extensive survey of indentation crack …

… In summary, we investigated the complex morphology of subsurface cracking induced by
Vickers indentation in a glass ceramic … The details of crack shape could be imaged by nano-CT, …

… In this review, the author’s works on indentation-induced deformation and cracking in glass
… how a crack nucleates during the indentation, direct observation of a contact region between …

… Many observations in glass-ceramic indentation experiments … A direct probing of deformation
evolution under contact … of cracks for the glass-ceramics sample. This is not to say that the …

… Direct observation of crack growth in soda-lime-silica glass by a video … = =0.8–0.9) which
is earlier than observed in this study (Fig. 4). In another … Subcritical crack growth in ceramics …

… , whereas no cracks can be obtained in more than 50% of the indentation imprints for the …
obtained glass-ceramic, we can also eliminate the mechanisms for crack resistance observed …

… as metals, ceramics and glasses became … analysis of the irreversible deformation process
allows for an estimation of the driving force for indentation cracking, as well as for the crack …

… and crack initiation of chemically strengthened soda-lime silicate and sodium aluminosilicate
glasses during lateral indentation and scratch testing. Instrumented indentation using a …

… of plastic deformation during indentation of silicate glasses. We … registered in the indentation
of silicate glasses will be … in relation to crack formation in silicate glasses. Our conclusion is …

… direction.5, 12, 14 Direct observation of lateral crack initiation at the trailing edge (ie, after
the sliding indenter has passed) has been made by Bulsara and Chandrasekar on glass.15 …