Residual stress and crack initiation in laser clad composite layer with Co-based alloy and WC+ NiCr

C Lee, H Park, J Yoo, C Lee, WC Woo, S Park - Applied Surface Science, 2015 - Elsevier
Although laser cladding process has been widely used to improve the wear and corrosion
resistance, there are unwanted cracking issues during and/or after laser cladding. This study …
被引用次数：138 相关文章

Residual stress and crack initiation in laser clad composite layer with Co-based alloy and WC+ NiCr

C Lee, H Park, J Yoo, C Lee… - Applied Surface …, 2015 - ui.adsabs.harvard.edu
Although laser cladding process has been widely used to improve the wear and corrosion
resistance, there are unwanted cracking issues during and/or after laser cladding. This study …

Residual stress and crack initiation in laser clad composite layer with Co-based alloy and WC+ NiCr

C Lee, H Park, J Yoo, C Lee, WC Woo… - Applied Surface Science, 2015 - inis.iaea.org
[en] Highlights:• Major problem, clad cracking in laser cladding process, was researched.•
Residual stress measurements were performed quantitatively by neutron diffraction method …

Residual stress and crack initiation in laser clad composite layer with Co-based alloy and WC plus NiCr

C Lee, H Park, J Yoo, C Lee… - APPLIED SURFACE …, 2015 - repository.hanyang.ac.kr
Although laser cladding process has been widely used to improve the wear and corrosion
resistance, there are unwanted cracking issues during and/or after laser cladding. This study …

Residual stress and crack initiation in laser clad composite layer with Co-based alloy and WC+ NiCr

C Lee, H Park, J Yoo, C Lee, WC Woo, S Park - Applied Surface Science, 2015 - infona.pl
Although laser cladding process has been widely used to improve the wear and corrosion
resistance, there are unwanted cracking issues during and/or after laser cladding. This study …