To evaluate the effect of scaling procedures using different ultrasonic tips on the surface roughness, color stability and bacterial accumulation of lithium disilicate ceramic. Scaling procedure was carried out using ultrasonic scaler (Satalec, Acteon, North America) with stainless-steel tip (US), titanium tip (UT) and plastic tip (UP), on disc shaped lithium disilicate samples cemented into a cavity prepared onto the labial surface of freshly extracted bovine teeth (10 samples per group). The samples were stored in coffee solution in an incubator at 37 C for 12 days, which is equivalent to 1 year of coffee consumption. The surface roughness was measured before and after the scaling procedure using a profilometer and atomic force microscopy. The color parameters were measured before and after scaling and staining procedures using VITA Easyshade Advance 4.0 according to the CIE L* a* b* color order system. The samples were then incubated with Streptococcus mutans (S. mutans) suspension. After incubation, the plates with 30 to 300 typical colonies of S. mutans were counted in a colony counter and mean values of colony forming units were obtained (CFU/mL). The titanium scaling tip showed a statistically significant higher mean values of change in surface roughness ΔRa and bacterial count than the plastic scaling tip. Color changes (ΔE) were not a statistically significant among the groups. The results showed a statistically significant positive (direct) correlation between surface roughness