… In summary, we have significantly improved the room temperature power factor of Cu 2 Se
thin films prepared by the thiol-amine dissolution process by a post treatment process which …

… highest power factor for a solution processed Cu2Se thin film reported at room temperature.
… summary, we have significantly improved the room temperature power factor of Cu2Se thin …

… recognized as cutting-edge TE materials for applications near room temperature (RT) [3,4]. …
along with improved electrical properties. With increasing T s the stoichiometric ratios of Cu …

… the deposition temperature and stoichiometric ratios. These … At room temperature, the power
factor of the unannealed … materials, the power factor of Cu 2 Se thin films remains relatively …

… and further leading to the enhancement of power factor. … 400 K, the room-temperature α-phase
Cu 2 Se has high carrier … was investigated to improve the thin films’ crystallinity and then …

… with uniform element distribution was fabricated at room temperature … power factor of 9.23
μWcm −1 K −2 is achieved for α-Cu 2 Se … [2] With the rapid rise of portable and wearable …

… The highest power factor of 15.6 μ W/cmK 2 was achieved for … that of all Cu 2 Se thin films,
sputtered at different power. … S/cm at room temperature [20]. Out of the deposition methods as …

… The power factor of the Cu 2 Se film on the rigid Al 2 O 3 substrate at 684 K is 0.62 … at room
temperature using the TDTR method. The maximum ZT value is 0.073 at 374 K. With the rapid …

… the film deposited at - 0.4 V showed the peaks of Cu2Se after … a buffer layer and on rapid
thermal annealing in S. … growth from aqueous media at room temperature to be preferable. …

… thermoelectric power factor to that of the polycrystalline films … a high ZT of 0.68 at near room
temperature (RT).Therein, the … one of the reasons why a-Cu2Se NWs exhibited a high S2s in …