Reducibility of ceria under steam reforming conditions and the effect of particle size on its reducibility was examined using two ceria samples with distinctly different mean particle sizes (3.5 nm versus 120 nm), but with similar polyhedral morphologies. The degree of reduction from Ce⁴⁺ to Ce³⁺ was characterized by temperature programmed reduction (TPR) and in situ X-ray absorption near edge structure spectroscopy (XANES) where the nanopolyhedra were observed to reduce much more readily compared to the larger particle-size sample. There was also significant reduction of the nanopolyhedra under ethanol steam reforming conditions. Ceria nanopolyhedra exhibited significantly more Ce³⁺ sites which contributed to a lower occurrence of surface acidic sites. The acidic/basic sites were probed by probe molecules such as pyridine and CO₂ through in situ diffuse reflectance infrared spectroscopy (DRIFTS). The particle size also showed major differences in the steam reforming activity of ceria, with nanopolyhedra with a 3.5-nm mean particle size exhibiting significantly higher carbon cleavage and ethanol dehydration activity than its counterpart of 120 nm mean particle size.