High tensile strength ultra high molecular weight polyethylene (UHMWPE) fibers were
prepared via the dry spinning method. Raw material was UHMWPE resin with 6 million …

Rodlike samples were made from four kinds of poly (ethylene‐co‐vinyl alcohol)(EVAL)
pellets with different ethylene contents. From these rodlike samples, fibers were produced …

A liquid isothermal bath (LIB) was introduced into the high-speed melt spinning process of
poly (vinylidene fluoride)(PVDF) to modify the temperature and stress profiles in the spinning …

Firstly, the effects of the spinning temperature, spinning voltage, tip-to-collector distance and
ambient temperature on the diameter of melt-electrospinning polypropylene (PP) fibers were …

The monofilaments were prepared by melt-spinning under different quench temperatures.
The thermal properties were investigated by Differential scanning calorimetry (DSC) and the …

The high-speed spinning process of poly (ethylene terephthalate)(PET) was modified by
introducing a liquid isothermal bath (LIB) which was kept at a temperature of 155° C and …

Melt electrospinning is a much more simple and safe method to produce ultra fine fibers than
solution electrospinning. The diameters of melt electrospinning fibers are thicker. To find the …

Melt spinning is a widely used process for producing polymeric filaments. It involves feeding
polymer pellets or granules into an extruder, melting the polymer, and forcing the melted …

Technical and hygienic nonwovens, originating typically from fossil‐based synthetic
polymers, are the fastest growing applications in the textile industry. Recently developed …