Stress analysis and failure mechanisms of plasma-sprayed thermal barrier coatings
J Yang, L Wang, D Li, X Zhong, H Zhao… - Journal of Thermal Spray …, 2017 - Springer
Yttria-stabilized zirconia coatings were deposited by plasma spraying and heat-treated at
1100° C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
1100° C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings
J Yang, L Wang, D Li, X Zhong… - International Thermal …, 2016 - dl.asminternational.org
Yttria stabilized zirconia coatings were deposited by plasma spraying and heat treated in air
at 1100° C for 50-200 h. Residual stresses in the ceramic topcoat and the thermally grown …
at 1100° C for 50-200 h. Residual stresses in the ceramic topcoat and the thermally grown …
Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings.
J Yang, L Wang, D Li, X Zhong… - Journal of Thermal …, 2017 - search.ebscohost.com
Yttria-stabilized zirconia coatings were deposited by plasma spraying and heat-treated at
1100 C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
1100 C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings
J Yang, L Wang, D Li, X Zhong, H Zhao… - Journal of Thermal Spray …, 2017 - infona.pl
Yttria-stabilized zirconia coatings were deposited by plasma spraying and heat-treated at
1100° C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
1100° C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings
J Yang, L Wang, D Li, X Zhong… - Journal of Thermal …, 2017 - ui.adsabs.harvard.edu
Yttria-stabilized zirconia coatings were deposited by plasma spraying and heat-treated at
1100 C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
1100 C for 50, 100, 150, and 200 h in air, respectively. Mechanical properties including …
Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings
J Yang, L Wang, D Li, X Zhong, H Zhao, S Tao - ITSC 2016, 2016 - dl.asminternational.org
Yttria stabilized zirconia coatings were deposited by plasma spraying and heat treated in air
at 1100 C for 50-200 h. Residual stresses in the ceramic topcoat and the thermally grown …
at 1100 C for 50-200 h. Residual stresses in the ceramic topcoat and the thermally grown …