The effects of sintering temperature on superconductivity of prepared by hot pressing
Q Wang, L Li, Y Zhao, H Zhang… - International Journal of …, 2020 - World Scientific
The MgB 2 superconductor bulks were prepared by hot-pressing under the pressure of 55
MPa at different temperatures of 650∘ C, 700∘ C, 800∘ C, 900∘ C, 1000∘ C, respectively …
MPa at different temperatures of 650∘ C, 700∘ C, 800∘ C, 900∘ C, 1000∘ C, respectively …
The effects of sintering temperature on superconductivity of MgB2 prepared by hot pressing.
Q Wang, L Li, Y Zhao, H Zhang… - International Journal of …, 2020 - search.ebscohost.com
The MgB 2 superconductor bulks were prepared by hot-pressing under the pressure of 55
MPa at different temperatures of 650∘ C, 700∘ C, 800∘ C, 900∘ C, 1000∘ C, respectively …
MPa at different temperatures of 650∘ C, 700∘ C, 800∘ C, 900∘ C, 1000∘ C, respectively …
The effects of sintering temperature on superconductivity of MgB2 prepared by hot pressing
Q Wang, L Li, Y Zhao, H Zhang… - International Journal of …, 2020 - ui.adsabs.harvard.edu
The MgB2 superconductor bulks were prepared by hot-pressing under the pressure of 55
MPa at different temperatures of 650∘ C, 700∘ C, 800∘ C, 900∘ C, 1000∘ C, respectively …
MPa at different temperatures of 650∘ C, 700∘ C, 800∘ C, 900∘ C, 1000∘ C, respectively …