Ultrasonic impact treatment to improve stress corrosion cracking resistance of welded joints of aluminum alloy
J Yu, G Gou, L Zhang, W Zhang, H Chen… - Journal of Materials …, 2016 - Springer
Stress corrosion cracking is one of the major issues for welded joints of 6005A-T6 aluminum
alloy in high-speed trains. High residual stress in the welded joints under corrosion results in …
alloy in high-speed trains. High residual stress in the welded joints under corrosion results in …
[引用][C] Ultrasonic Impact Treatment to Improve Stress Corrosion Cracking Resistance of Welded Joints of Aluminum Alloy
J Yu, G Gou, L Zhang, W Zhang, H Chen… - Journal of Materials …, 2016 - cir.nii.ac.jp
[引用][C] Ultrasonic Impact Treatment to Improve Stress Corrosion Cracking Resistance of Welded Joints of Aluminum Alloy
J Yu, L Zhang, W Zhang, G Gou, H Chen… - Journal of Materials …, 2016 - elibrary.ru
[PDF][PDF] Ultrasonic Impact Treatment to Improve Stress Corrosion Cracking Resistance of Welded Joints of Aluminum Alloy
J Yu, G Gou, L Zhang, W Zhang, H Chen… - Journal of Materials …, 2016 - researchgate.net
Stress corrosion cracking is one of the major issues for welded joints of 6005A-T6 aluminum
alloy in highspeed trains. High residual stress in the welded joints under corrosion results in …
alloy in highspeed trains. High residual stress in the welded joints under corrosion results in …
Ultrasonic Impact Treatment to Improve Stress Corrosion Cracking Resistance of Welded Joints of Aluminum Alloy
J Yu, G Gou, L Zhang, W Zhang, H Chen… - Journal of Materials …, 2016 - infona.pl
Stress corrosion cracking is one of the major issues for welded joints of 6005A-T6 aluminum
alloy in high-speed trains. High residual stress in the welded joints under corrosion results in …
alloy in high-speed trains. High residual stress in the welded joints under corrosion results in …
Ultrasonic Impact Treatment to Improve Stress Corrosion Cracking Resistance of Welded Joints of Aluminum Alloy
J Yu, G Gou, L Zhang, W Zhang… - Journal of Materials …, 2016 - ui.adsabs.harvard.edu
Stress corrosion cracking is one of the major issues for welded joints of 6005A-T6 aluminum
alloy in high-speed trains. High residual stress in the welded joints under corrosion results in …
alloy in high-speed trains. High residual stress in the welded joints under corrosion results in …