[HTML][HTML] On the high fracture toughness of wood and polymer-filled wood composites–Crack deflection analysis for materials design
E Jungstedt, MVT Da Costa, S Östlund… - Engineering Fracture …, 2024 - Elsevier
Cracks oriented in the toughest direction across the grain of wood (0°) tend to deflect at 90°
to the precrack rather than extending in 0° direction. Fracture toughness data across the …
to the precrack rather than extending in 0° direction. Fracture toughness data across the …
On the high fracture toughness of wood and polymer-filled wood composites–Crack deflection analysis for materials design
E Jungstedt, MV Tavares da Costa… - Engineering Fracture …, 2024 - diva-portal.org
Cracks oriented in the toughest direction across the grain of wood (0◦) tend to deflect at 90◦
to the precrack rather than extending in 0◦ direction. Fracture toughness data across the …
to the precrack rather than extending in 0◦ direction. Fracture toughness data across the …
On the high fracture toughness of wood and polymer-filled wood composites–Crack deflection analysis for materials design
E Jungstedt, M Vinícius Tavares Da Costa… - Engineering Fracture …, 2024 - diva-portal.org
Cracks oriented in the toughest direction across the grain of wood (0) tend to deflect at 90 to
the precrack rather than extending in 0 direction. Fracture toughness data across the grain …
the precrack rather than extending in 0 direction. Fracture toughness data across the grain …