[PDF][PDF] Synthesis and optical properties of large-area single-crystalline 2D semiconductor WS2 monolayer from chemical vapor deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo, C Qiu… - academia.edu
TION www. MaterialsViews. com www. advopticalmat. de perfect triangular shape and sharp
edges are effectively formed on the 300 nm SiO 2/Si substrate through the CVD process. It is …
被引用次数：696 相关文章

Synthesis and optical properties of large-area single-crystalline 2D semiconductor WS2 monolayer from chemical vapor deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo, C Qiu… - 2013 - dr.ntu.edu.sg
Large-area triangular single crystals of WS2 monolayer are synthesised from a chemical
vapor deposition process and their optical properties are systematicly studied. This work …

[引用][C] Synthesis and Optical Properties of Large-Area Single-Crystalline 2D Semiconductor WS2 Monolayer from Chemical Vapor Deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo, C Qiu… - 2014 - hero.epa.gov
Synthesis and Optical Properties of Large-Area Single-Crystalline 2D Semiconductor WS2
Monolayer from Chemical Vapor Deposition | Health & Environmental Research Online (HERO) …

[引用][C] Synthesis and Optical Properties of Large-Area Single-Crystalline 2D Semiconductor WS2Monolayer from Chemical Vapor Deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo… - Advanced Optical …, 2013 - cir.nii.ac.jp
Synthesis and Optical Properties of Large-Area Single-Crystalline 2D Semiconductor WS<sub>2</sub>Monolayer
from Chemical Vapor Deposition | CiNii Research CiNii 国立情報学研究所 学術情報 …
[PDF] ntu.edu.sg

[PDF][PDF] Synthesis and Optical Properties of Large-Area Single-Crystalline 2D Semiconductor WS 2 Monolayer from Chemical Vapor Deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo, C Qiu… - 2013 - spms.ntu.edu.sg
TION www. MaterialsViews. com www. advopticalmat. de perfect triangular shape and sharp
edges are effectively formed on the 300 nm SiO 2/Si substrate through the CVD process. It is …

[引用][C] Synthesis and Optical Properties of Large‐Area Single‐Crystalline 2D Semiconductor WS2 Monolayer from Chemical Vapor Deposition

C Cong, J Shang, X Wu, B Cao… - Advanced Optical …, 2014 - Wiley Online Library
TION www. MaterialsViews. com www. advopticalmat. de perfect triangular shape and sharp
edges are effectively formed on the 300 nm SiO 2/Si substrate through the CVD process. It is …

Synthesis and optical properties of large-area single-crystalline 2D semiconductor WS2 monolayer from chemical vapor deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo, C Qiu… - 2014 - scholarbank.nus.edu.sg
Synthesis and optical properties of large-area single-crystalline 2D semiconductor WS2
monolayer from chemical vapor deposition | ScholarBank@NUS Skip navigation NUS …
[PDF] ntu.edu.sg

[PDF][PDF] Synthesis and Optical Properties of Large-Area Single-Crystalline 2D Semiconductor WS 2 Monolayer from Chemical Vapor Deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo, C Qiu… - 2013 - spms.ntu.edu.sg
TION www. MaterialsViews. com www. advopticalmat. de perfect triangular shape and sharp
edges are effectively formed on the 300 nm SiO 2/Si substrate through the CVD process. It is …

Synthesis and optical properties of large-area single-crystalline 2D semiconductor WS2 monolayer from chemical vapor deposition

C Cong, J Shang, X Wu, B Cao, N Peimyoo, C Qiu… - 2013 - dr.ntu.edu.sg
Large-area triangular single crystals of WS2 monolayer are synthesised from a chemical
vapor deposition process and their optical properties are systematicly studied. This work …