Numerical analyses of the residual stress and top coat cracking behavior in thermal barrier coatings under cyclic thermal loading

J Jiang, W Wang, X Zhao, Y Liu, Z Cao… - Engineering Fracture …, 2018 - Elsevier
Acting as one of the original cracks for interfacial delamination, the horizontal roughness-
induced top coat crack plays an important role in the premature failure of the air plasma …