The characterization of microstructure and texture development of binary Mg-0.3Ce (wt%) after equal-channel angular pressing (ECAP) processing via route Bc at 300 and 350 °C through 4 passes were investigated using electron backscatter diffraction (EBSD) measurements. The results demonstrated an effective grain refinement from millimeter range to 6.7 and 8.3 μm obtained after 4 passes at 300 and 350 °C, respectively. The grain refinement was obtained through dynamic recrystallization (DRX). At 300 °C, DRX occurred at low strain by twin-induced dynamic recrystallization (TDRX) and particle stimulated nucleation (PSN) mechanism and then converted with increasing strain to sub-grain development (SD) and grain boundary bulging dynamic recrystallization (GBBDRX). Besides, grain growth occurred during processing at 350 °C. The texture development strongly depends on the strain level, deformation temperature and DRX mechanisms. At 300 °C, a typical basal texture with a deviation of 40° towards extrusion direction was formed gradually up to 4 passes while a completely different texture was formed at 350 °C due to the large grain size.