The corrosion resistances of near equimolar CoCrFeMnNi magnetron-sputtered thin films with different carbon concentrations were examined in 0.05 M HCl and 0.05 M H₂SO₄. Polarization curves were recorded with different scan rates with and without reducing the native oxide. The results showed that the carbon concentration and the experimental conditions affected the electrochemical behaviour mainly in the Cr transpassive region. At potentials above 850 mV, the carbon-containing films were more corrosion resistant in 0.05 M HCl than in 0.05 M H₂SO₄ due to a lower carbon oxidation rate in 0.05 M HCl, facilitating the formation of a Mn-rich oxide layer.