Samarium doped zinc-magnesium-phosphate glasses having composition (60 – x)P₂O₅–10MgO–30ZnO–xSm₂O₃ where x = 0.1, 0.3, 0.6, 1.0 mol % were prepared by melt quenching technique. Archimedes method was used to measure their densitieswhich are lying in the range 2.65–2.91 g/cm³. On the basis of the increasing trend in the density while increasing the content of Sm₂O₃ it can be concluded that the bridging oxygen is converted to non-bridging oxygen The UV-Vis absorption spectroscopy was carried on in the wavelength range 310–900 nm where the absorption spectra consist of six absorption peaks corresponding to the transitions from the ground state ⁶H_5/2 to various excited energy levels. The optical band gaps are calculated to be 3.93–4.41 eV, 3.31–3.73 eV and 0.27–0.29 eV for direct band gap, indirect band gap and Urbach energy, respectively. The physical parameters like oxygen packing density, refractive index, molar refractivity, metallization, and electronic polarizability are also studied. The Differential Scanning Calorimetry (DSC) technique is used to evaluate the thermal stability.