In this paper, the results of the electrical, noise, and optical characterization of p-i-n and p-B-i-n diodes with AlSb and 4 ML AlSb/8 ML GaSb superlattice barriers in High-Operating Temperature conditions, are presented. Experimental and theoretical noise parameters were compared. Both dark current and noise analysis showed that the p-B_{p_bulk}-i-n bariode had the best performance. P-i-n photodiodes had the highest experimental value of specific detectivity (D*) of 6.16 × 10⁹ Jones at 210 K and zero bias. At about −1 V reverse bias, the bariode with AlSb/GaSb electron barrier caught up to it and both devices achieved D* = (1–1.1) × 10⁸ Jones. Further optimization of the superlattice-based electron barrier should result in the improvement of bariode performance at a smaller bias, at which better noise performance is more pronounced. It was shown that neglecting the low-frequency noise component can lead to a significant overestimation of detectivity. The simple method of incorporation of low-frequency noise contribution in the detectivity calculation, without time-consuming measurements, has been proposed.