Validity of Toughness Measurements From Miniature Specimens Failing in Different Fracture Modes
S Ortner, M Sanchez, J Echols… - Journal of …, 2024 - asmedigitalcollection.asme.org
Using miniature compact tension (mini-C (T))(4 mm thick, 0.16 T) specimens to determine
toughness in reactor pressure vessel (RPV) steels permits the ductile-to-brittle transition
temperature to be derived from small amounts of material and allows more effective use of
surveillance specimens. However, questions have been raised as to whether the failure
mechanisms are the same in miniature and large specimens, something that must be
ensured when transferring fracture results obtained in mini-C (T) specimens to larger …
toughness in reactor pressure vessel (RPV) steels permits the ductile-to-brittle transition
temperature to be derived from small amounts of material and allows more effective use of
surveillance specimens. However, questions have been raised as to whether the failure
mechanisms are the same in miniature and large specimens, something that must be
ensured when transferring fracture results obtained in mini-C (T) specimens to larger …
Validity of Toughness Measurements From Miniature Specimens Failing in Different Fracture Modes
Using miniature compact tension (mini-C (T))(4 mm thick, 0.16 T) specimens to determine
toughness in reactor pressure vessel (RPV) steels permits the ductile-to-brittle transition
temperature to be derived from small amounts of material and allows more effective use of
surveillance specimens. However, questions have been raised as to whether the failure
mechanisms are the same in miniature and large specimens, something that must be
ensured when transferring fracture results obtained in mini-C (T) specimens to larger …
toughness in reactor pressure vessel (RPV) steels permits the ductile-to-brittle transition
temperature to be derived from small amounts of material and allows more effective use of
surveillance specimens. However, questions have been raised as to whether the failure
mechanisms are the same in miniature and large specimens, something that must be
ensured when transferring fracture results obtained in mini-C (T) specimens to larger …