The present work concerns the residual stresses in plasma-sprayed ZrO2-7Y2O3 thermal
barrier coatings deposited on Ni-base superalloy substrates which were kept at different …

Superalloy samples were coated with thermal barrier coatings (TBC). This TBC-system
consisted of two layers. The first layer was a vacuum-plasma sprayed, corrosion resistant …

Residual stresses in plasma-sprayed coatings were studied by three experimental
techniques: curvature measurements, neutron diffraction and X-ray diffraction. Two distinct …

Superalloy samples (IN 738) were coated with thermal barrier coatings (TBC). This TBC-
system consisted of two layers. The first layer was a vacuum-plasma-sprayed, corrosion …

Thermal barrier coating (TBC) specimens have been prepared by plasma spraying. A
vacuum plasma spray (VPS) MCrAlY bond coat and atmospheric plasma spray (APS) …

Thermal barrier coatings consisting of a NiCrAlY bond coating and a 1.4 mm thick partially
stabilised zirconia top coating were air plasma sprayed onto grit blasted nickel-base …

Nanostructured and traditional thermal barrier coatings have been prepared by
atmospherical plasma spraying (APS) on NiCrAlY-coated superalloy substrates …

Failure in plasma-sprayed thermal barrier coatings systems mostly takes place in the
ceramic topcoat or at the interface between the topcoat and the bondcoat. The failure …

Various combinations of plasma sprayed bond coatings and zirconia ceramic coatings on a
nickel-base superalloy substrate were tested by static thermal exposure at 1200/sup 0/C and …

This paper presents a thorough study on plasma sprayed 8 wt% Y 2 O 3-stabilized ZrO 2
(8YSZ) thermal barrier coatings intended to show the effect of the internal microstructure …