Transitions into the magnetically ordered state in function of the average A-cation radius,〈
rA〉, have been studied by neutron powder diffraction for (La1− yPry) 0.7 Ca0. 3MnO3 …

A series of (La1− yPry) 0.7 Ca0. 3MnO3 samples with y= 0.5, 0.6, 0.7 and 0.75 has been
systematically studied by neutron powder diffraction. The analysis shows that their basic …

The effect of oxygen isotope substitution on the alternating-current magnetic susceptibility for
(La 1-y Pr y) 0.7 Ca 0.3 MnO 3 ceramics (y= 0, 0.25, 0.5, 0.75, 1) was studied in the …

Raman spectroscopic studies were carried out in the oxygen-isotope exchanged (La1−
xNdx) 0.7 Ca0. 3MnO3. We found that the phonon frequency and width are different for the …

Emission Mössbauer effect investigations were done simultaneously with resistivity
measurements on two similar samples of La 0.8 Ca 0.2 Mn (57 Co) O 3, in one of which 18 O …

High resolution neutron diffraction shows that the mesoscopic separation into ferromagnetic
(FM) and antiferromagnetic (AFM) phases and the FM transition temperature TC in the …

In this paper a detailed study of the La 1− x Ca x MnO 3 () phase diagram using powder x-
ray diffraction and magnetization measurements is presented. The lack of well characterized …

The CMR compound La1− x CaxMnO3 shows a transition to commensurate charge ordering
(Mn3+–Mn4+) for x= 50%. In the range x= 42–50%, the high temperature paramagnetic …

Since the possibility of an intrinsically phase-separated ground state in mixed-valent
manganites was suggested by theoretical studies, 1–3 much experimental effort has gone …

Oxygen isotope effect in magnetic properties of CMR manganites of the (La1− yPry) 0.7 Ca0.
3MnO3 system was systematically studied. Substitution of 16O by 18O was found to stabilize …