Effect of isochronal annealing on the microstructure, texture and mechanical properties of a cold-rolled high manganese steel
S Pramanik, AA Saleh, EV Pereloma… - Materials …, 2018 - Elsevier
Abstract A Fe-17Mn-3Al-2Si-1Ni-0.06 C wt.% steel was subjected to cold-rolling to 42%
thickness reduction and isochronally annealed for 300 s between 500 and 850° C. The high …
thickness reduction and isochronally annealed for 300 s between 500 and 850° C. The high …
Effect of isochronal annealing on the microstructure, texture and mechanical properties of a cold-rolled high manganese steel
S Pramanik, AA Saleh, EV Pereloma, AA Gazder - 2018 - ro.uow.edu.au
Abstract A Fe-17Mn-3Al-2Si-1Ni-0.06 C wt.% steel was subjected to cold-rolling to 42%
thickness reduction and isochronally annealed for 300 s between 500 and 850 C. The high …
thickness reduction and isochronally annealed for 300 s between 500 and 850 C. The high …
Effect of isochronal annealing on the microstructure, texture and mechanical properties of a cold-rolled high manganese steel
S Pramanik, AA Saleh, EV Pereloma… - Materials …, 2018 - hero.epa.gov
Abstract A Fe-17Mn-3Al-2Si-lNi-0.06 C wt.% steel was subjected to cold-rolling to 42%
thickness reduction and isochronally annealed for 300 s between 500 and 850 degrees C …
thickness reduction and isochronally annealed for 300 s between 500 and 850 degrees C …
Effect of isochronal annealing on the microstructure, texture and mechanical properties of a cold-rolled high manganese steel
S Pramanik, AA Saleh, EV Pereloma… - Materials …, 2018 - osti.gov
Highlights:• Recrystallised γ grains have similar orientations to reverted/recovered γ grains.•
After reversion, γ orientations are correlated to ε and α′-martensite orientations.• γ …
After reversion, γ orientations are correlated to ε and α′-martensite orientations.• γ …
Effect of isochronal annealing on the microstructure, texture and mechanical properties of a cold-rolled high manganese steel
S Pramanik, AA Saleh, EV Pereloma… - Materials …, 2018 - inis.iaea.org
[en] Highlights:• Recrystallised γ grains have similar orientations to reverted/recovered γ
grains.• After reversion, γ orientations are correlated to ε and α′-martensite orientations.• γ …
grains.• After reversion, γ orientations are correlated to ε and α′-martensite orientations.• γ …
[PDF][PDF] Effect of isochronal annealing on the microstructure, texture and mechanical properties of a cold-rolled high manganese steel
S Pramanik, AA Saleh, EV Pereloma, AA Gazder - core.ac.uk
Abstract A Fe-17Mn-3Al-2Si-1Ni-0.06 C wt.% steel was subjected to cold-rolling to 42%
thickness reduction and isochronally annealed for 300 s between 500 and 850 C. The high …
thickness reduction and isochronally annealed for 300 s between 500 and 850 C. The high …
[PDF][PDF] Research Online
S Pramanik, AA Saleh, EV Pereloma, AA Gazder - ro.uow.edu.au
Abstract A Fe-17Mn-3Al-2Si-1Ni-0.06 C wt.% steel was subjected to cold-rolling to 42%
thickness reduction and isochronally annealed for 300 s between 500 and 850 C. The high …
thickness reduction and isochronally annealed for 300 s between 500 and 850 C. The high …