Abstract β-Solidifying γ-TiAl based alloys have gained scientific attention and showed potential applications as structure materials. When adding the β-stabilizing elements (eg, Nb …
F Kong, N Cui, Y Chen, X Wang - Metallurgical and Materials Transactions …, 2018 - Springer
Beta-gamma TiAl alloys are promising light-weight structural materials for use in high- temperature applications. Disordered β phase at high temperature is beneficial to the hot …
S Xu, M Reid, KD Liss, Y Xu, H Zhang, J He, J Lin - Intermetallics, 2020 - Elsevier
Three alloys with composition range of Ti-(25–35) Al (atomic%) were in-situ investigated using neutron diffraction to clarify the phase stability and equilibria in the Ti-rich part of the Ti …
O Rios, S Goyel, MS Kesler, DM Cupid, HJ Seifert… - Scripta Materialia, 2009 - Elsevier
Ti–Al–Nb alloys have shown promising properties for high-temperature applications. Although the phase diagram for this system has been well researched, there is still …
A Grytsiv, P Rogl, H Schmidt, G Giester, P Hundegger… - Intermetallics, 2004 - Elsevier
Ternary compounds formed by Ti and Al with transition metals of the eighth group have been investigated by X-ray powder/single crystal and neutron powder diffraction. Two series of …
C Li, H Guo, L Zheng, J Yang, L Ye, L Liu, L Zhang - Processes, 2023 - mdpi.com
Phase equilibria in the Ti-Nb-Mn ternary system at 1173K, 1273K and 1373K were studied through the equilibrated alloy method by using scanning electron microscopy (SEM) …
H Xu, XB Li, WW Xing, L Shu, YC Ma, K Liu - Journal of Materials Science & …, 2019 - Elsevier
The phase transformation behavior of an as-cast Ti-42Al-5 Mn (at.%) alloy after subsequent quenching from 1380° C to 1000° C was investigated based on the differential thermal …
XM Huang, GM Cai, HS Liu - Journal of Materials Science, 2022 - Springer
Abstract TiAl-or Ti 3 Al-based alloys have gained industrial applications in recent years. The incorporation of β-stabilizing element Ta has demonstrated to better adjust their …
A new intermetallic phase γ1 was determined in the TiAl+ Nb composition area in the Ti–Al– Nb ternary system. The chemical formula of γ1 phase was determined to be Ti4Nb3Al9. The …