Photorefractive Effect in CdSSe: V Crystals
SH Morgan, M Davis, Z Pan, KT Chen… - MRS Online …, 1997 - cambridge.org
We present two-wave mixing results obtained with CdSSe: V crystals. A large photorefractive
gain of 0.24 cm-1 was observed at 633 nm with an optical intensity of 60 mW/cm2 and a …
gain of 0.24 cm-1 was observed at 633 nm with an optical intensity of 60 mW/cm2 and a …
Photorefractive Effect in CdSSe: V Crystals
SH Morgan, M Davis, Z Pan, KT Chen, H Chen… - MRS Online …, 1997 - Springer
We present two-wave mixing results obtained with CdSSe: V crystals. A large photorefractive
gain of 0.24 cm-1 was observed at 633 nm with an optical intensity of 60 mW/cm 2 and a …
gain of 0.24 cm-1 was observed at 633 nm with an optical intensity of 60 mW/cm 2 and a …
PHOTOREFRACTIVE EFFECT IN CdSSe: V CRYSTALS STEVEN H. MORGAN, MICHELLE DAVIS, ZHENGDA PAN, KUO-TONG CHEN, HENRY CHEN, SWANSON L …
SH MORGAN, M DAVIS, Z PAN, KUOT CHEN, H CHEN… - cambridge.org
We present two-wave mixing results obtained with CdSSe: V crystals. A large photorefractive
gain of 0.24 cm'was observed at 633 nm with an optical intensity of 60 mW/cm2 and a …
gain of 0.24 cm'was observed at 633 nm with an optical intensity of 60 mW/cm2 and a …