AS Zuruzi, H Li, G Dong - Materials Science and Engineering: A, 1999 - Elsevier
The effect of surface roughness on the properties of Al6061 joints fabricated by diffusion bonding in air at 450° C was studied. It was found that rougher surfaces yield superior …
ASF Britto, JS Binoj - Revista de Metalurgia, 2022 - revistademetalurgia.revistas.csic.es
Diffusion bonding has been successfully used to join dissimilar high-strength aluminium alloys. In bonding AA2014 with AA7075 aluminium alloy, the main diffusion bonding process …
S Venugopal, M Seeman, R Seetharaman… - International Journal of …, 2022 - Elsevier
Diffusion bonding is a sort of solid-state joining that allows the joining of metals with similar and dissimilar compositions by allowing them to diffuse into one another. The current study …
S Habisch, M Böhme, S Peter, T Grund, P Mayr - Metals, 2018 - mdpi.com
Diffusion bonding is a well-known technology for a wide range of advanced joining applications, due to the possibility of bonding different materials within a defined …
The precipitation-hardenable aluminum alloy 6061 (AA 6061) is favored for aerospace components and automotive parts. However, the tenacious oxide layer on the surface …
A Ismail, P Hussain, M Mustapha… - Journal of Mechanical …, 2018 - ir.uitm.edu.my
A direct diffusion bonding of marine grade aluminium alloy AA6061 and steel A36 was carried out in an argon environment at 640° C. Specimens were heated in a furnace for a …
A Ureña, JMG De Salazar, J Quiñones - Journal of materials science, 1992 - Springer
Diffusion bonds between alumina and high-strength aluminium alloy (AA-7075) have been produced and studied in the present work. Direct diffusion bonding in the solid state was …
J Varmazyar, M Khodaei - Journal of Alloys and Compounds, 2019 - Elsevier
Diffusion bonding, due to improving the dispersion of brittle intermetallic compounds, reducing the process energy and increasing the bonding strength of aluminum-magnesium …
F Wu, W Zhou, Y Han, X Fu, Y Xu, H Hou - Materials, 2018 - mdpi.com
Three different bonding couples assembled by two commonly used aerospace aluminum alloys were bonded within the temperature range of 460–520° C under 6 MPa for 60 min in …