J Languillaume, G Kapelski, B Baudelet - Acta Materialia, 1997 - Elsevier
The influence of cold wire drawing on the structure of a pearlitic steel containing 0.7 wt% of carbon and subjected to a strain of approximately 3.5 has been studied. The as-deformed …
J Languillaume, G Kapelski, B Baudelet - Materials Letters, 1997 - Elsevier
Tensile tests were performed on heavily cold drawn and annealed pearlitic steel wires, on which wire drawing induced a partial dissolution of the cementite phase. The high strength …
X Zhang, A Godfrey, N Hansen, X Huang - Acta Materialia, 2013 - Elsevier
The microstructure and crystallography of drawn pearlitic steel wires have been quantified by a number of electron microscopy techniques including scanning electron microscopy …
J Takahashi, M Kosaka, K Kawakami, T Tarui - Acta Materialia, 2012 - Elsevier
Atom probe tomography analysis of heavily drawn pearlitic steel wires was performed with and without low-temperature aging. In the as-drawn wire, the lamellar cementite hardly …
X Zhang, A Godfrey, X Huang, N Hansen, Q Liu - Acta Materialia, 2011 - Elsevier
Strengthening mechanisms and strength–structure relationships have been analyzed in a cold-drawn pearlitic steel with a structural scale in the nanometer range and a flow stress of …
WJ Nam, CM Bae, SJ Oh, SJ Kwon - Scripta Materialia, 2000 - Elsevier
Cold drawing is an effective process to increase the strength of fully pearlitic steels with an acceptable level of ductility. Recently, it has been reported that the lamellar cementite …
K Van Acker, J Root, P Van Houtte, E Aernoudt - Acta Materialia, 1996 - Elsevier
The residual stress state in both the cementite and ferrite phases of cold-drawn pearlitic wires has been measured by neutron diffraction. The phase microstress in the axial direction …
Cold-drawing of a pearlitic steel results in a dramatic increase in its ultimate tensile strength, to> 3.2 GPa, and it retains ductility (1, 2). Typically, such a pearlitic wire is produced by fully …
X Zhang, A Godfrey, N Hansen, X Huang, W Liu… - Materials …, 2010 - Elsevier
The evolution of the cementite phase during wet wire drawing of a pearlitic steel wire has been followed as a function of strain. Particular attention has been given to a quantitative …