Kinetics of pearlite spheroidization
P Matusiewicz, J Augustyn-Nadzieja… - Archives of Metallurgy …, 2017 - yadda.icm.edu.pl
The pearlite spheroidization in Fe-0.76% C high purity steel was investigated. The samples
of a coarse pearlite microstructure were isothermal annealed at 700, 680, 660, 640 and 620 …
of a coarse pearlite microstructure were isothermal annealed at 700, 680, 660, 640 and 620 …
recrystallization of ferrite in spheroidite of Fe-0.67% c steel
P Matusiewicz, W Ratuszek… - Archives of Metallurgy …, 2011 - yadda.icm.edu.pl
In this paper the study of ferrite recrystallization in Fe-0.67% C carbon steel with
microstructure of the coarse spher-oidite was performed. The purpose of the investigations …
microstructure of the coarse spher-oidite was performed. The purpose of the investigations …
[PDF][PDF] Assessment of pearlite degradation in power industry cast steel after long-term exploitation
J Kasińska, P Matusiewicz, A Czarski… - Inżynieria …, 2017 - academia.edu
The paper presents the results of pearlite degradation analysis. The degradation level was
evaluated on three specimens (cuttings) of low alloyed 20HM cast steel, sampled from …
evaluated on three specimens (cuttings) of low alloyed 20HM cast steel, sampled from …
[PDF][PDF] Spatial distribution of cementite particles in Fe-0.67% C steel
P Matusiewicz, A Czarski - Archives of Metallurgy and Materials, 2013 - bibliotekanauki.pl
The particles arrangement in material space is represented by point field determined by the
particle reference points, ie, particle centers which can be described by the pair-correlation …
particle reference points, ie, particle centers which can be described by the pair-correlation …
[PDF][PDF] Kinetics of pearlite spheroidization
A Czarski, T Skowronek, P Matusiewicz… - Archives of Metallurgy …, 2017 - journals.pan.pl
The pearlite spheroidization in Fe-0.76% C high purity steel was investigated. The samples
of a coarse pearlite microstructure were isothermal annealed at 700, 680, 660, 640 and 620 …
of a coarse pearlite microstructure were isothermal annealed at 700, 680, 660, 640 and 620 …
Zależność między twardością a mikrostrukturą stali Fe-0, 67% C ze skoagulowanym cementytem
P Matusiewicz, K Wiencek, A Czarski - Hutnik, Wiadomości Hutnicze, 2011 - infona.pl
Przedmiotem pracy jest ocena wpływu parametrów mikrostruktury ze skoagulowanym
cementytem na twardość stali Fe-0, 67% C. W stali o mikrostrukturze grubego sferoidytu w …
cementytem na twardość stali Fe-0, 67% C. W stali o mikrostrukturze grubego sferoidytu w …