Investigations of the fatigue performance of composite materials have accompanied their
introduction in several engineering domains since the 1950s. An abundance of publications …

The influence of the constant life diagram (CLD) formulation on the fatigue life prediction of
composite materials was examined. Most commonly used and recently proposed CLDs …

Many of the stiffness-based fatigue damage models contain four main limitations for
composite materials life determination:(i) lack of capability in simulating the whole periods of …

Fatigue and residual strength data available in literature were modeled with a modified two-
parameter wear-out model based on strength degradation. The model explicitly accounts for …

The demand to capture translaminar crack growth under fatigue loading scenarios led this
work contribution to carry out the Finite Fracture Mechanics (FFM) method in fatigue damage …

High-cycle fatigue features of over 108 cycles, particularly the initiation and propagation of
edge delamination considering the effects of transverse cracks, were investigated using …

Fatigue failure of carbon fiber-reinforced plastics (CFRPs) under cyclic loadings has
attracted the attention of researchers recently. In this study, the entropy-based failure …

The change of fatigue damage behavior depending on an applied stress level in carbon
fiber reinforced plastic (CFRP) laminates was evaluated quantitatively in this study. To …

Accelerated axial fatigue testing of carbon fiber reinforced plastics quasi-isotropic laminate
by using ultrasonic fatigue testing machine In addition, higher stress amplification should be …

The influence of damage accumulation metric, constant life diagram formulation and cycle
counting method on life prediction schemes for composite materials under variable …