Improving the resistance of high-strength steel to SCC in a SO2-polluted marine atmosphere through Nb and Sb microalloying
A series of high-strength steels microalloyed with Nb and Sb were prepared via vacuum
melting and hot rolling, and their resistance to stress corrosion cracking (SCC) was …
melting and hot rolling, and their resistance to stress corrosion cracking (SCC) was …
Microbiologically influenced corrosion: a review of the studies conducted on buried pipelines
Buried pipelines are essential for the delivery of potable water around the world. A key
cause of leaks and bursts in these pipelines, particularly those fabricated from carbon steel …
cause of leaks and bursts in these pipelines, particularly those fabricated from carbon steel …
Influence of different heat-affected zone microstructures on the stress corrosion behavior and mechanism of high-strength low-alloy steel in a sulfurated marine …
The stress corrosion cracking (SCC) behavior and mechanism of the simulated heat-affected
zone (HAZ) of high-strength low-alloy (HSLA) steel in a sulfurated marine atmosphere were …
zone (HAZ) of high-strength low-alloy (HSLA) steel in a sulfurated marine atmosphere were …
Comparative study of the stress corrosion behavior of a multiuse bainite steel in the simulated tropical marine atmosphere and seawater environments
Stress corrosion cracking (SCC) behavior of a multiuse high-strength low-alloy (HSLA)
bainite steel was comparatively studied in the simulated seawater and marine atmosphere …
bainite steel was comparatively studied in the simulated seawater and marine atmosphere …
[HTML][HTML] Corrosion and SCC initiation behavior of low-alloy high-strength steels microalloyed with Nb and Sb in a simulated polluted marine atmosphere
Corrosion and stress corrosion cracking (SCC) behavior of some low-alloy high-strength
steels microalloyed with Nb and Sb were in detail studied in a simulated polluted marine …
steels microalloyed with Nb and Sb were in detail studied in a simulated polluted marine …
Investigation of subsea oil pipeline rupture
M Azzam, W Khalifa - Engineering failure analysis, 2023 - Elsevier
In the current work, a full-bore rupture in the form of a fast-running ductile fracture has
occurred at an 18-inch offshore pipeline in the subsea portion. The pipeline was constructed …
occurred at an 18-inch offshore pipeline in the subsea portion. The pipeline was constructed …
Crack growth degradation-based diagnosis and design of high pressure liquefied natural gas pipe via designable data-augmented anomaly detection
D Yang, S Lee, J Lee - Journal of Computational Design and …, 2023 - academic.oup.com
A new approach to anomaly detection termed “anomaly detection with designable
generative adversarial network (Ano-DGAN)” is proposed, which is a series connection of a …
generative adversarial network (Ano-DGAN)” is proposed, which is a series connection of a …
Investigation of erosion-corrosion failure of API X52 carbon steel pipeline
A failure analysis of API X52 steel pipeline was conducted. The investigation included
complete material characterizations using tensile and hardness testing, optical microscope …
complete material characterizations using tensile and hardness testing, optical microscope …
Electrochemical characteristic and stress corrosion behavior of API X70 high-strength pipeline steel under a simulated disbonded coating in an artificial seawater …
The electrochemical and stress corrosion cracking (SCC) behavior of API X70 pipeline steel
under a disbonded coating in artificial seawater was studied using in situ electrochemical …
under a disbonded coating in artificial seawater was studied using in situ electrochemical …
A novel metaheuristic-based approach for prediction of corrosion characteristics in offshore pipelines
Corrosion is recognized as the primary cause of structural damage and collapse. While
numerous studies can be found that imply a decent local prediction, they lack …
numerous studies can be found that imply a decent local prediction, they lack …