The effects of sintering and shot peening processes on the fatigue strength
Alumix 431 metal powders have been used in this study since they are widely used in the
industrial applications. First, Alumix 431 powders were compacted at 400 MPa pressure …
industrial applications. First, Alumix 431 powders were compacted at 400 MPa pressure …
Investigation of fatigue properties of shot peened and plasma nitrocarburized P/M FC0205 steel
One of the widely used powder metal materials in automotive industry, which is copper steel
FC 0205 (Fe+ 2% Cu+ 0.5% C), was used in this study. The pressed samples has been …
FC 0205 (Fe+ 2% Cu+ 0.5% C), was used in this study. The pressed samples has been …
[PDF][PDF] EFFECT OF SHOT PEENING PROCESS ON ALUMIX 431 POWDER MATERIALS
Ç ARCH - academia.edu
In this work, Alumix 431 metal powders have been chosen for study due to widely used in
the industrial applications. First, Alumix 431 powders were pressed at 400 MPa pressure …
the industrial applications. First, Alumix 431 powders were pressed at 400 MPa pressure …
Effect Of Shot Peening Process On Alumix 431 Powder Materials
Bu çalışmada, endüstriyel uygulamalarda yaygın olarak kullanılan Alumix 431 tozları
seçilmiştir. Alumix 431 tozları 400 MPa basınç ve oda sıcaklığında sıkıştırılmıştır. Daha …
seçilmiştir. Alumix 431 tozları 400 MPa basınç ve oda sıcaklığında sıkıştırılmıştır. Daha …
[PDF][PDF] BİLYALI DÖVME İŞLEMİ VE YÜKSEK SICAKLIĞIN, BAKIR İLAVELİ TOZ METAL ÇELİK PARÇALARIN YORULMA DAYANIMINA ETKİSİNİN İNCELENMESİ
Değişken gerilmeler altında çalışan makine parçalarının, yorulma dayanımı değerlerinin
arttırılması için bilyalı dövme işlemleri pratikte endüstriyel anlamda yaygın olarak …
arttırılması için bilyalı dövme işlemleri pratikte endüstriyel anlamda yaygın olarak …