Low-cycle fatigue behavior of U71Mn rail steel with pre-corrosion
Z Fu, Y Sun, Y Hu, R Chen, P Wang, Q Kan - Engineering Failure Analysis, 2025 - Elsevier
Rail steels that are extensively exposed to the humid natural environment increasingly
experience corrosion fatigue, emerging as a potential and hazardous failure mode. This …
experience corrosion fatigue, emerging as a potential and hazardous failure mode. This …
[HTML][HTML] Microstructure Tailoring of Laser Powder Bed Fused 316L Impellers for Enhanced Mechanical Properties and Optimum Electrochemical Characteristics …
Y Aghayar, A Shahriari, M Shakerian, M Purdy… - Materials Science and …, 2025 - Elsevier
This study investigates the design, manufacturing, and post-processing of 316L stainless
steel impellers fabricated using laser powder bed fusion (LPBF) for optimum mechanical …
steel impellers fabricated using laser powder bed fusion (LPBF) for optimum mechanical …
TVMS calculation model for gear tooth tip chipping failure with EHL
S Wu, Y Zhou, W Xing, Y Liu, X Chen - Engineering Failure Analysis, 2025 - Elsevier
This paper proposes a calculation method for Time-Varying Mesh Stiffness (TVMS) in the
presence of tooth tip chipping defects under elastohydrodynamic lubrication (EHL). A …
presence of tooth tip chipping defects under elastohydrodynamic lubrication (EHL). A …
Rotating Bending Fatigue of Laser Powder Bed Fused 316L Stainless Steel at Various Stress Levels: Microstructural Evaluation and Predictive Modeling
This research studies the effect of variable stress levels on the rotating bending fatigue
(RBF) tests of 316L stainless steel fabricated by the laser powder bed fusion (LPBF) method …
(RBF) tests of 316L stainless steel fabricated by the laser powder bed fusion (LPBF) method …
Rotating Bending Fatigue Durability of Wrought 304 Stainless Steel: A Comparative Study of Surface-Treated vs. Untreated Specimen
A Behvar, O Scott-Emuakpor, K James… - Journal of Design …, 2024 - minerva-aset.com
The rotating bending fatigue test, which is a common durability test for industrial
components, was employed in this study to examine the impact of the surface treatment …
components, was employed in this study to examine the impact of the surface treatment …