The high-temperature compressive deformation behavior of a Cu-10 wt.% Sn solid solution
alloy was studied in the temperature range of 843–993 K and in the strain rate range of 10 …

Abstract The Al-Mg-Mn-Sc-Zr alloy is taken as the object and the tensile deformation
behaviors at 298 K–673 K are studied in this research. By comparing the evolutions of flow …

The asymmetric feeder die extrusion was introduced on high strength Al-Zn-Mg alloy. The
hot extrusion experiments were carried out using flat die without feeder, with symmetric and …

The paper presents an investigation that was conducted to determine the possibility of the
occurrence of the process of dynamic recrystallization in 2024 alloy during monotonic tensile …

Hot torsion tests were performed on the Al-7Mg alloy at the temperature ranging from 300 to
500° C and strain rates between 0.05 and 5 s− 1 to explore the progressive dynamic …

The flow behavior of the AA5052 alloy in a fully annealed state was analyzed across a range
of temperatures: 25, 100, 200, and 300° C, and five strain rates: 0.001, 0.005, 0.01, 0.05, and …

This study examined the effects of the strain rate on the texture evolution of Al-6Mg alloys
over one hour of annealing at 300° C. Three different strain rates of 0.1 s− 1, 1 s− 1, and 10 …

We investigate the benefits and limitations of mesoscale models for discontinuous dynamic
recrystallization (DDRX) in pure copper at elevated temperature with the two-fold aim of …

7055 aluminum alloy is widely used in manufacture of key components in fields of
aerospace. Hot forming is the vital process for manufacture of components. Dynamic …

The hot deformation behavior of advanced reduced-activation alloy (ARAA) was
investigated using hot torsion tests. The flow stress decreased as deformation temperature …