H Gu, P Yan, L Jiao, S Chen, Y Song, S Zou… - International Journal of …, 2023 - Elsevier
The service performance of hole surface is directly tied to its machining-induced surface integrity which is usually produced by sequential operations. Due to its conformal geometry …
In this paper, we present the first numerical analysis upon the effect of heterogeneity on the stresses in fretting fatigue problems. We analyze the stress distribution in heterogeneous …
Q Yang, W Zhou, P Gai, X Zhang, X Fu, G Chen, Z Li - Wear, 2017 - Elsevier
Abstract In this study, Ti-6Al-4V dovetail joint specimens which highly simulate the attachment between the blade and disk of fan stages in a certain gas turbine engine were …
S Vantadori, A Zanichelli - Fatigue & Fracture of Engineering …, 2021 - Wiley Online Library
In the last decades, many alleviation measures were proposed in order to improve the life of fretting fatigue‐affected components. In such a context, the shot peening treatment is worth …
J Wu, D Liu, Y Guan, H Shi, S Cheng, J Shi… - Engineering Fracture …, 2023 - Elsevier
To improve surface integrity and suppress fretting fatigue of bolt-connected 2024HDT alloy plate-hole structure, the effect of shot peening forming (SPF) and shot peening …
C Navarro, J Vázquez, J Domínguez - International Journal of fatigue, 2017 - Elsevier
The initial crack path is analysed in a series of fretting fatigue tests with cylindrical contact. In such tests, both specimens and pads are made of Al7075-T651 alloy and a non-proportional …
This paper analyses the initial crack path in a fretting fatigue test of Al7075-T651 alloy with a cylindrical contact and compares the capability of some multiaxial fatigue criteria to predict …
M Moreno-Rubio, D Erena, J Vázquez, C Navarro - Tribology International, 2024 - Elsevier
Fretting fatigue manifests in mechanical systems exposed to contact forces that vary over time, resulting in premature cracks that can lead to component failure. Shot peening …
The effect of a rough, textured surface and contact orientations on the fretting behavior of self- mated martensitic 34CrNiMo6+ QT steel was examined via a large annular flat-on-flat …