This paper presents a review of the current state of scientific understanding of the corrosion
phenomenon known as Hydrogen-Induced Cracking (HIC). HIC is defined as cracking in low …

Utilization and transportation of hydrogen energy are considered an inevitable trend toward
achieving global zero CO 2 emission. It is predicted that the utilization and storage of natural …

In this work, the microstructures of an X80 pipeline steel were characterized, and their
susceptibilities to hydrogen-induced cracking (HIC) were investigated by hydrogen …

Hydrogen-induced cracking (HIC) susceptibility tests, hydrogen permeation tests and the
electron backscatter diffraction (EBSD) measurements were used to study the effect of Nb on …

Mechanism of failure by hydrogen induced cracking (HIC) in pipeline steel has not been
extensively investigated in the past. In the present work, an API X70 pipeline steel was …

Hydrogen induced cracking (HIC) in pipeline steels industry causes a huge amount of
economic loss to the industry, but despite this, HIC behavior is still not fully understood. We …

This work studied the determination of the hydrogen fugacity during electrolytic charging.
With a virgin surface, there were irregular permeation transients, attributed to irreproducible …

In this investigation, the hydrogen permeation experiment was used to determine the
parameters for diffusion, and the hydrogen microprint technique was used to visualize the …

The effect of different partial pressures of H2S ([Formula: see text]) on the hydrogen
permeation behaviour of API-X52 pipeline carbon steel was investigated in a high …

Hydrogen induced cracking (HIC) behaviour was investigated in three layers of RD–ND
plane. HIC test showed that all cracks initiated from the mid-thickness of the RD–ND plane …