Recently, it has been suggested that the future designs of implants and endoprothesis
should be focused on the use of a new generation of biocompatible, corrosion and wear …

The corrosion resistance of Ti-5% Ta-2% Nb alloy and DOCTOR (double oxide coating on
titanium for reconditioning) coated titanium by O5+ ion irradiation were compared and …

Titanium alloy beta 21S was implanted with oxygen ions by plasma immersion ion
implantation. The implanted surface was characterized by micro-Raman, XPS and FESEM …

Titanium or titanium alloys are very attractive materials for use as biomedical materials. Non-
toxic elements of oxygen, calcium and phosphorus were implanted into titanium and the …

The corrosion assessment and surface layer properties after O5+ ion irradiation of
commercially pure titanium (CP-Ti) has been studied in 11.5 N HNO3. CP-Ti specimen was …

利用同步辐射光电子能谱(SR-XPS) 原位研究了经3 keV O2 溅射的SUS 304 不锈钢中Fe, Ni, Cr
合金元素与氧离子的化学反应活性差异及一种金属元素间的相互作用规律 …

In the present investigation, polished samples were implanted with nitrogen ion at an energy
of 60keV and implantation doses were 1× 1016, 5× 1016, 1× 1017 and 6× 1017ions/cm2 …

The aim of this paper is to study the effect of niobium ion implantation on corrosion
resistance and phase formation on the implanted surfaces of Ti–Al–Zr alloy. Niobium ion …

Titanium alloys have attracted more attention as biomaterials. Plasma ion implantation is
utilized in this paper to improve the bioactivity, wear resistance, and corrosion resistance of …

Titanium or titanium alloys are very attractive biomedical materials. Biocompatible elements
of oxygen, calcium and phosphorus were implanted into titanium and changes of surface …