The ultra-fine grained (UFG) CoCrFeMnNi alloy (Cantor alloy) exhibits high mechanical
strength. As far as its real application is concerned, the corrosion behavior of the UFG …

Intergranular corrosion (IGC) behaviors of X65-Inconel 625 clad pipe welded joints of
different thickness (1.5, 2.0, 2.5 mm) were investigated. Corrosion tests showed that as the …

Abstract Effect of Te on the corrosion behavior of GH3535 alloy in molten LiF-NaF-KF
(FLiNaK) salt at 700℃ was investigated. GH3535 alloy only suffered from uniform corrosion …

The effect of lanthanum (La) addition on the tellurium (Te) induced embrittlement of Ni-16Mo-
7Cr alloy was studied in this work. The addition of La element can significantly decrease the …

High-entropy alloys (HEAs) are currently considered as promising materials for a wide range
of applications, including high-temperature use. Since HEAs contain a large number of …

The corrosion properties of Alloy 625 have been studied in molten FLiNaK salt for 48 h at
700° C as a function of tellurium (Te) concentrations using immersion tests and …

The influence of yttrium (Y) addition on the tellurium (Te) induced intergranular
embrittlement of Ni-16Mo-7Cr alloy was investigated. The results show that the addition of Y …

The catastrophic intergranular cracking had been observed in the low-Cr alloy components
in the primary loop of molten salt reactor. Such cracking was related to the coupling effect of …

In this study, pure Ni was demonstrated to protect the GH3535 alloy from Te vapor corrosion
because of its strong absorption capacity. Severe Te corrosion of a single GH3535 alloy …

The effect of Al addition on Te diffusion behavior of a Ni-16Mo-7Cr base superalloy was
investigated at 800° C for 100 h. The results show that Ni 3 Te 2 and Cr 3 Te 4 are the …